Alloy T-800 Koluboti-orisun Alloy elo Properties 

Ohun elo

COBALT alloy T-800

Kemikali tiwqn

K: 16.5 ~ 18.5%; Ni+Fe: ≤3.0%; Mo: 27.5 ~ 31.5%; C: ≤0.5%; N: ≤0.07%; Si: ≤3.5%; P: ≤0.03%; S: ≤0.03%; Co: iyokù

Awọn ohun-ini ohun elo

Agbara fifẹ σb: 1793 MPa, modulus rirọ σs: 2412 MPa, lile lile fifọ: 115 MPa·m^ 1/2, lile HRC: 54～62, iwuwo: ≥8.2g/cm3.

Awọn abuda akọkọ

T800 jẹ ọkan ninu awọn ohun elo ti o da lori koluboti ti o wọpọ julọ. Ẹya ti o tobi julọ ni olùsọdipúpọ edekoyede kekere, ati pe o ni resistance yiya ti o dara julọ, resistance ipata ati resistance otutu giga.

T 800 koluboti-orisun alloys wa ni kq lile intermetallic yellow (Laves) awọn ipele tuka ni a Aworn eutectic tabi ri to ojutu matrix. Wọn ṣe afihan yiya ti o dara julọ ati resistance ijagba, resistance ipata giga ati pe o dara ni pataki fun awọn ipo lubrication ti o nira. Iyara yiya ti awọn ohun elo Tribaloy da lori iwọn iwọn didun ti ipele Laves.

Tribaloy T-800 ti a ṣe lati koju ga otutu yiya ati abrasion. Nitori akoonu chromium giga rẹ, o ni ifoyina ti o dara julọ ati idena ipata. T-800 le ati ki o ni dara yiya resistance ju T-400.

T-800 ṣe afihan idiwọ ipata to dara julọ ni acetic acid (50% ifọkansi, farabale) ati phosphoric acid (85% ifọkansi, 66 ° C). O tayọ ipata resistance ni a tun ṣe akiyesi ni sulfuric acid (5% ifọkansi, 66°C).

Awọn ohun elo

T-800 jẹ lilo pupọ ni ile-iṣẹ afẹfẹ nitori wiwọ otutu otutu ti o ga ati resistance galling, ni pataki ni lile ti awọn abẹfẹlẹ ẹrọ tobaini ọkọ ofurufu. Ni afikun, o tun lo lati ṣe iṣelọpọ tabi wọ awọn ẹya pupọ ni yiya giga ati awọn agbegbe ipata, gẹgẹbi awọn bearings, awọn kamẹra, awọn oruka idaduro, awọn oruka piston Diesel, awọn edidi ẹrọ, awọn ijoko ti o nii, awọn gige valve ati awọn paati fifa.